Columnar to Equiaxed Transition in Peritectic TiAl Based Alloy Studied by a Power-Down Technique
| Autor: | Shaun McFadden, Juraj Lapin, Zuzana Gabalcová, Ulrike Hecht, Robin P. Mooney |
|---|---|
| Rok vydání: | 2014 |
| Předmět: |
Equiaxed crystals
Hypergravity Work (thermodynamics) Titanium aluminide Materials science Mechanical Engineering Metallurgy Alloy engineering.material Condensed Matter Physics Power (physics) chemistry.chemical_compound Cooling rate chemistry Mechanics of Materials Etching (microfabrication) engineering General Materials Science |
| Zdroj: | Materials Science Forum. :193-198 |
| ISSN: | 1662-9752 |
| Popis: | Columnar to equiaxed transition (CET) was studied in a peritectic TiAl-based alloy with chemical composition Ti-45.1Al-4.9Nb-0.25C-0.2B (at.%). Solidification experiments were conducted in a Bridgman-type apparatus using cylindrical moulds made of high-purity Y2O3. The methodology containing appropriate etching and observations under flat light in stereo-microscope was used to identify the morphology of primary β phase grains and position of CET in the samples˰ All samples prepared by power down-technique showed sharp CET. The position of the CET measured from the beginning of the sample depends on the applied cooling rate and increases from approximately 65 to 115 mm by decreasing cooling rate from 50 to 15 K/min. Based on terrestrial experiments, the future work focused on microgravity and hypergravity CET experiments and numerical modeling is proposed. A Bridgman furnace front tracking method will be applied in future work to complement the experimental results here as part of the European Space Agency GRADECET programme. This modeling will input directly into planned microgravity and hypergravity CET experiments. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|