Thermoanalytical and morphologic study of gel-grown silver (I) chromate single crystals
Autor: | A. Lentz, W. Büchele |
---|---|
Rok vydání: | 1987 |
Předmět: | |
Zdroj: | Crystal Research and Technology. 22:27-33 |
ISSN: | 1521-4079 0232-1300 |
DOI: | 10.1002/crat.2170220109 |
Popis: | Rhombic single crystals of silver (I) chromate were grown in silica gels. They were of tabular shape with a size of a = 0.3, b = 30 and c = 3 mm. The morphology of the crystals was interpreted by a detailed discussion of the structure. Silver (I) chromate consists of (100) layers connected along the a-axis by silver atoms in octahedral coordination. The crystals were characterized by their powder diffraction data. Differential thermal analysis studies were made by use of single crystals. The enthalpy of the phase transformation taking place at 485.2 °C is found to be ΔHtr = 8.8 kJ/mol. Mittels der Geltechnik konnten tafelformige orthorhombische Einkristalle von Silber(I)-chromat gezuchtet werden. Sie erreichten eine Grose von a = 0.3, b = 30 and c = 3 mm. Die Morphologie der Kristalle wurde anhand einer eingehenden Strukturbetrachtung interpretiert. Silber(I)chromat besteht aus (100) Schichten, die uber Silberatome in oktaedrischer Koordination verknupft sind. Die Kristalle wurden anhand der Pulverdaten identifiziert. An den Einkristallen wurden DTA-Messungen vorgenommen. Die Enthalpie der Phasenumwandlung bei 485.2 °C wurde mit ΔHtr = 8.8 kJ/mol ermittelt. |
Databáze: | OpenAIRE |
Externí odkaz: |
načítá se...