Crosslinking poly[1-(trimethylsilyl)-1-propyne] (PTMSP) films with 3,3′-diazidodiphenylsulfone, a bis(azide) crosslinker, rendered the films insoluble in common solvents for PTMSP such as toluene. At all temperatures, mixed gas CH 4 and n -C 4 H 10 permeabilities of crosslinked PTMSP were less than those of uncrosslinked PTMSP, which correlates with lower free volume in the crosslinked material. The presence of fumed silica (FS) nanoparticles in both uncrosslinked PTMSP and crosslinked PTMSP increased mixed gas CH 4 and n -C 4 H 10 permeabilities, consistent with the disruption of polymer chain packing by such nanoparticles. Mixed gas CH 4 permeabilities of all films were significantly less than their corresponding pure gas CH 4 permeabilities. For example, at 35 °C, the mixed gas CH 4 permeabilities were approximately 60–80% less than their pure gas values. The greatest decrease was observed for uncrosslinked PTMSP, while nanocomposite PTMSP films showed the least decrease. The mixed gas n -C 4 H 10 /CH 4 selectivities of crosslinked PTMSP and nanocomposite PTMSP films were less than those of uncrosslinked PTMSP at all temperatures. For example, at 35 °C, the mixed gas n -C 4 H 10 /CH 4 selectivities of uncrosslinked PTMSP, crosslinked PTMSP containing 10 wt% crosslinker, and uncrosslinked PTMSP containing 30 wt% FS were 33, 27, and 17, respectively, when the feed gas contained 2 mol% n -C 4 H 10 and the total upstream mixture fugacity was 11 atm. For all films, as temperature decreased, mixed gas n -C 4 H 10 permeabilities increased, and mixed gas CH 4 permeabilities decreased. Consequently, the mixed gas n -C 4 H 10 /CH 4 selectivities increased substantially as temperature decreased and the mixed gas selectivity of uncrosslinked PTMSP increased from 33 to 170 as temperature decreased from 35 °C to −20 °C when the feed gas contained 2 mol% n -C 4 H 10 and the total upstream mixture fugacity was 11 atm. |
Full Text from ScienceDirect