Self-made tension machine was used to measure the evolution of recovery stress under different processing state for NiTiNb alloy. Then, SEM was used to investigate the microstructure evolution. The results show that the range of the highest recovery stress for forged NiTiNb alloy is between 210-215MPa. Otherwise, the recovery stress level of the samples enduring cold drawing and hot rolling is basically same, which all belong to the rage of 210-220MPa. After forging, the firstly precipitated TiNi phase particles become fine, only 5-8μm. The Nb tablets in eutectic microstructure, which originally contributed between TiNi phase particles, appear spheroidization. |