Electrolyte design for Li metal-free Li batteries
Autor: | Ji Chen, Qin Li, Xiulin Fan, Chunsheng Wang, Travis P. Pollard, Oleg Borodin |
---|---|
Rok vydání: | 2020 |
Předmět: |
Materials science
Mechanical Engineering Nucleation chemistry.chemical_element 02 engineering and technology Electrolyte Current collector 010402 general chemistry 021001 nanoscience & nanotechnology Condensed Matter Physics 01 natural sciences Cathode 0104 chemical sciences law.invention Bismuth Anode Chemical engineering chemistry Mechanics of Materials law General Materials Science 0210 nano-technology Faraday efficiency Electrochemical potential |
Zdroj: | Materials Today. 39:118-126 |
ISSN: | 1369-7021 |
Popis: | Li metal, with the lowest thermodynamically achievable negative electrochemical potential and the highest specific capacity (3860 mAh g−1), is the ultimate anode choice for Li batteries. However, the highest reported Li plating/stripping Coulombic efficiency (CE) of 99.5% after extensive efforts is still too low for the Li metal-free (all the Li metal in cycling comes from cathode, without anode pre-lithiation) Li metal batteries. The low CE is attributed to both non-uniform Li plating/stripping on the lithiophobic Cu current collector and Li dendrite growth through lithiophilic organic–inorganic solid electrolyte interphase (SEI) formed in carbonate electrolytes. Here, we use a lithiophilic Bismuth graphite blend (Bi–Gr) substrate to replace lithiophobic Cu current collector to seed a uniform Li nucleation, and form a lithiophobic LiF-rich SEI rather than lithiophilic organic-rich SEI to suppress Li dendrite growth. Molecular dynamics simulations reveal the preferential reduction of anions in 2.0 M LiPF6 in tetrahydrofuran/2-methyl tetrahydrofuran (2.0 M LiPF6–mixTHF) electrolyte to generate LiF-rich SEI on plated Li. Bi–Gr substrate and 2.0 M LiPF6–mixTHF electrolyte enable the Li anodes to achieve a record high CE of 99.83% at a high capacity of 1.0 mAh cm−2 and current of 0.5 mA cm−2. The Bi particles serve as dispersed nucleation centers that promote uniform Li deposition with strong adhesion to the substrate to avoid dead Li, while the lithiophobic LiF-rich SEI promotes lateral Li growth and suppresses the vertical Li dendrite growth even at a high current density of 3.0 mA cm−2 and high areal capacities of 3.0 mAh cm−2. The regulation of Li nucleation and growth enables the Li metal-free LiFePO4 full cells to achieve 100 cycles at a practical areal capacity of >2.0 mAh cm−2. This manuscript highlights the benefits of simultaneous substrate design to improve Li nucleation and electrolyte design to promote lithiophobic SEI growth, enabling a promising and practical route Li metal-free Li metal batteries. |
Databáze: | OpenAIRE |
Externí odkaz: |