Autor: | V. A. Udovenko, I. Yu. Khmelevskaya, P. L. Potapov, S. D. Prokoshkin, V. Ya. Abramov, Yu. V. Blinov |
---|---|
Rok vydání: | 2000 |
Předmět: |
Materials science
Metallurgy Alloy Metals and Alloys Titanium alloy Shape-memory alloy engineering.material Atmospheric temperature range Condensed Matter Physics Hysteresis Mechanics of Materials Diffusionless transformation engineering Coupling (piping) Deformation (engineering) Composite material |
Zdroj: | Metal Science and Heat Treatment. 42:353-356 |
ISSN: | 0026-0673 |
Popis: | 1. Shape-memory alloy Ti - 45% Ni - 10% Nb with a wide hysteresis of the martensitic transformation can be used for thermomechanical coupling of pipelines. Disassembled thermomechanical clutches can be stored at room temperature and assembled with heating to a temperature somewhat exceedingt room; the joint can be easily disassembled by RSME under deep cooling. 2. Treatment of alloy Ti - 45% Ni - 10% Nb by the recommended method provides the following characteristics of shape recovery: a reversible deformation of high-temperature SME of up to 8%, a degree of shape recovery of up to 60–80%, a temperature range of shape recovery from + 30 to + 90°C, and a reversible deformation of the RSME of 1–2%. 3. The deformation that induces the SME in the considered alloy can be performed from −10 to −70°C at e=10–12%; the thermomechanical clutches can be stored at a temperature of up to +30°C; the parts can be coupled with the help of a thermomechanical clutch in a temperature range from +30 to +100°C. The coupling is easily detachable after deep cooling due to the realization of the reversible SME. |
Databáze: | OpenAIRE |
Externí odkaz: |