Properties of Board Manufactured from Sawdust, Ricehusk and Charcoal
| Autor: | 황정우 ( Jung-woo Hwang ), 오승원 ( Seung-won Oh ) |
|---|---|
| Rok vydání: | 2020 |
| Předmět: | |
| Zdroj: | Journal of the Korean Wood Science and Technology. 48:61-75 |
| ISSN: | 2233-7180 1017-0715 |
| Popis: | In this study, the environmentally friendly material charcoal was added to ricehusk, an agricultural by-product, and sawdust, which emerges during the sawing process, to produce board by mixing ratio and concentration levels of ricehusk and charcoal; it then investigated its physical properties for development purposes and achieved the following results. The water absorption and thickness swelling of the compounded board produced per adding ratio of ricehusk and charcoal showed a gradually decreasing tendency along with the increase in adding ratio of the charcoal, and as the density of the compounded board increased, the water absorption decreased, while the thickness swelling increased. The internal bond strength of the compounded board had indicated its highest value of 0.49N/mm2 at the density of 0.7g/cm3. This satisfied the quality standard for KSF 3104 Particleboard. The internal bond strength of the compounded board manufactured per adding ratio of ricehusk and charcoal showed a steady decrease with the decrease in the adding ratio of ricehusk, and an increase in the addingratio of the charcoal. Also, in cases when the ratio of the ricehusk and charcoal by KSF 3104 quality standard were 35:5 and 30:10, it satisfied the quality standard of 15.0-type, whereas it satisfied the 13.0-type quality standard if the ratios were 25:15 and 20:20. It showed a tendency of increasing hardness of the compounded board with the increase in density, and decreasing hardness with the increase in the adding ratio of the charcoal. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|