| Popis: |
Martensitic stainless steel was chosen for a semi-solid processing due to high mechanical properties and resistance to high temperature surface oxidation. Modified H18 martensitic steel (1.1 % - C, 18.9 % - Cr, 0.1 % - V, 0.7 % - Mo, 0,9 % - Si, 2.0 % - Mn, balance Fe, all in weight %) modified with addition of 0.01 % boron was applied as a feedstock for semi-solid range temperature experiments. The samples were heated up to 1330°C to obtain about 26% of the liquid phase followed by rapid quenching in water. The microstructure of the samples consisted of austenitic globular grains (average grain size 42 μm, about 78 % of volume) surrounded by a eutectic mixture (ferrite, and M7C3,M23C6carbides as identified by X-ray and electron diffraction). The initial hardness of as-cast sample was 357 HV5and that after quenching from liquidus solidus range was 422 HV5. The X-ray analysis confirmed the presence of 16% - α-Fe, 80% - γ-Fe and 4% - M7C3carbides in rapid quenched sample. The EDS analysis of a eutectic mixture was as follows: 6.2 % - C, 31.7 % Cr, 0.1 % - Mn, 0.6 % - Si, 61.2 % Fe. The chemical composition analysis of globular grains confirmed the presence of 2.0% C, 16.3 % - Cr, 1 % - Si, 1.7 % - Mn, 0.5 % - Mo, 78.5% Fe. |