Effect of Al2O3 addition on texturing in a rotating strong magnetic field and densification of B4C
| Autor: | Anna V. Gubarevich, Tetsuo Uchikoshi, Tohru S. Suzuki, Ryosuke S.S. Maki, Toyohiko Yano, Katsumi Yoshida, Muhammad Fajar |
|---|---|
| Rok vydání: | 2019 |
| Předmět: |
Materials science
Spark plasma sintering chemistry.chemical_element Sintering 02 engineering and technology Boron carbide 01 natural sciences chemistry.chemical_compound 0103 physical sciences Materials Chemistry Ceramic Composite material Boron 010302 applied physics Rotating magnetic field Process Chemistry and Technology 021001 nanoscience & nanotechnology Microstructure Surfaces Coatings and Films Electronic Optical and Magnetic Materials chemistry visual_art Ceramics and Composites visual_art.visual_art_medium 0210 nano-technology Electron backscatter diffraction |
| Zdroj: | Ceramics International. 45:18222-18228 |
| ISSN: | 0272-8842 |
| Popis: | The properties of ceramics can be improved by controlling the microstructure through texturing ceramics in a strong magnetic field. Fabricating dense boron carbide (B4C) requires high temperature sintering, therefore sintering additives are often used in order to densify B4C ceramics at lower temperatures. However, combined effect of texturing and sintering additives on densification of B4C has not been made clear yet. Here we report the effect of alumina (Al2O3) sintering additive on texturing in a strong magnetic field and densification of B4C. Texturing was performed by rotating superconducting magnet at 12 T during slip casting process. Electron backscatter diffraction (EBSD) was used to observed the texturing projection. {0001} plane is clearly oriented in the plane parallel to rotating magnetic field. In addition, Lotgering factor was also calculated as quantitatively evaluation of texturing degree. Results on densification showed that addition of Al2O3 successfully increased density of B4C sintered by spark plasma sintering (SPS) at 1800oC to 97.8%. Formation of aluminum borate (Al5BO9) as secondary phase was detected by X-Ray diffraction (XRD). It is considered that the generation of Al5BO9 assisted finer densification of B4C ceramic. Textured B4C sintered at 1700oC by SPS without alumina addition exhibited the highest orientation of c-axis. Addition of alumina caused decrease in degree of orientation of c-axis. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect