Modification 3 of isotactic polybutene-1, prepared by crystallization from a solution at room temperature, was studied by dilatometric and X-ray examinations at different temperatures. At high degrees of crystallinity, its specific volume is intermediate between that of modification 1 and 2. By rapid heating its melting can be observed at about 102°C., while by a sufficiently slow heating it can even be totally converted into modification 1 before melting, by a solid-solid transformation. Modification 1 obtained in this way melts surprisingly low, at 109°C., probably because of morphological memory. During the melting of modification 3, or modification 1 originated by modification 3, crystallization of available liquid phase usually takes place, giving modification 2, which happens to be the most highly melting polymorph under these particular conditions. An der durch Kristallisation aus einer Losung bei Zimmertemperatur erhaltenen Modifikation 3 von isotaktischem Polybuten-1 wurden bei verschiedenen Temperaturen dilatometrische und rontgenographische Untersuchungen durchgefuhrt. Bei Hoher Kristallinitat liegt der Wert des spezifischen Volumens zwischen den Werten der Modifikation 1 und 2. Bei schnellem Aufheizen der Proben kann man bei etwa 102°C. ein Aufschmelzen beobachten, wahrend bei genugend kleiner Aufheizgeschwindigkeit vor dem Schmelzen im festen Zustand eine Umwandlung in die Modifikation 1 stattfindet. Die so erhaltene Modifikation 1 schmilzt uberraschend niedrig bei 109°C, wahrscheinlich wegen eines „morphologischen” Erinnerungs vermogens. Bereits wahrend des Schmelzens der Modifikation 3 – oder der aus der Modifikation 3 entstandenen Modification 1 – findet gewohnlich eine Kristallisation der entstehenden flussigen Phase statt. Man erhalt so die Modifikation 2, welche die unter diesen besonderen Bedingungen am hochsten schmelzende polymorphe Form dieses Polymeren darstellt. |
Plný text