Thermal Desorption Spectroscopy of (Ba, Sr)TiO3 Thin Films Prepared by Chemical Vapor Deposition
| Autor: | Kouichi Ono, Mikio Yamamuka, Akimasa Yuuki, Tetsuro Makita, Takaaki Kawahara |
|---|---|
| Rok vydání: | 1996 |
| Předmět: | |
| Zdroj: | Japanese Journal of Applied Physics. 35:729 |
| ISSN: | 1347-4065 0021-4922 |
| Popis: | Thermal desorption characteristics of (Ba, Sr)TiO3 [BST] thin films prepared by metalorganic chemical vapor deposition (CVD) using liguid sources have been studied, together with their crystallinity and electrical properties. Thermal desorption was observed for CO2 at 400° C and 900° C, and CO at 600° C. The intensities of the CO2 peaks at 400° C and 900° C increased with the increasing atomic composition ratio of (Ba+Sr)/Ti, in relation to the excess Ba and Sr in the BST films; in particular, the CO2 peak at 900° C may originate from BaCO3 and/or SrCO3 lumps formed in the films, and the CO2 peak at 400° C may be attributed to gases adsorbed on the sites of contaminants such as BaO x and/or SrO x in films, due to excess Ba and Sr coming from the atmosphere after deposition. On the other hand, the CO peak at 600° C occurred most strongly from BST films with high dielectric constants at (Ba+Sr)/Ti∼1, or perovskite crystalline structures having large grains. Moreover, the desorption of CO at 600° C was also observed from films kept in the atmosphere after annealed above 600° C in vacuum. These results imply that the BST crystalline perovskite grains may have adsorption sites for CO from the atmosphere. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|