| Popis: |
Polymer nanocomposite of multi-walled carbon nanotubes (MWCNT) nanoparticles incorporated with polylactic acid (PLA) and liquid natural rubber (LNR) as compatibilizer were prepared via melt blending method using the Haake Rheomix internal mixer. In order to obtain the optimal processing parameter, the nanocomposite with 89 wt % of PLA was blended with 10 wt % of LNR and 1 wt % of MWCNTs were mixed with various mixing parameter condition; mixing temperature, mixing speed and mixing time. The optimum processing parameter of the composites was obtained at temperature of 190°C, rotation speed of 90 rpm and mixing time of 14 min. Next, the effect of MWCNTs loading on the tensile properties of nanocomposites was investigated. The nanocomposites were melt blended using the optimal processing parameter with MWCNTs loading of 0.5, 1.0, 1.5, 2.0, 2.5, 3.0, 3.5 and 4 wt %. The result showed that the sample with 3.5 wt % of MWCNTs gave higher tensile strength and Young’s modulus. The SEM micrographs confirmed the effect of good dispersion of MWCNTs and their interfacial bonding in PLA nanocomposites. However, the elongation at break decreased with increasing the percentage of MWCNTs. |