Surface nanocrystallization treatment of AZ91D magnesium alloy by cold spraying shot peening process
| Autor: | Xiao-Bo Bai, Zhi-Hai Yi, Gang-Chang Ji, Hong-Tao Wang, Hai-Long Yao, Zhang Mengxian, Qing-Yu Chen |
|---|---|
| Rok vydání: | 2019 |
| Předmět: |
010302 applied physics
Materials science Alloy 02 engineering and technology Surfaces and Interfaces General Chemistry engineering.material 021001 nanoscience & nanotechnology Condensed Matter Physics Shot peening 01 natural sciences Indentation hardness Nanocrystalline material Surfaces Coatings and Films law.invention Optical microscope Transmission electron microscopy law 0103 physical sciences Materials Chemistry engineering Magnesium alloy Composite material 0210 nano-technology Diffractometer |
| Zdroj: | Surface and Coatings Technology. 374:485-492 |
| ISSN: | 0257-8972 |
| DOI: | 10.1016/j.surfcoat.2019.04.093 |
| Popis: | In this paper, a new cold spraying shot peening (CS-SP) technology was used to produce surface nanocrystallization (SNC) of AZ91D magnesium alloy for the first time. The structure characteristics of SNC layer on AZ91D alloy were investigated by means of X-ray diffractometer (XRD), optical microscopy (OM), scanning electronic microscopy (SEM) and transmission electron microscopy (TEM), respectively. The microhardness distribution of AZ91D specimen after CS-SP treatment was tested by a microhardness tester. The wear property and the coefficient of friction (COF) of AZ91D alloy before and after CS-SP treatment were investigated using the sliding wear tester. Experimental results showed that SNC layer with thickness about 40 μm can be prepared on AZ91D alloy by the CS-SP process. The average grain size of SNC layer was in range of 50–80 nm and a large number of deformation twin bands existed beneath the nanocrystalline layer. The microhardness of AZ91D specimen after CS-SP treatment exhibited a gradient distribution with the depth and the microhardness value of the outermost layer was up to 160 Hv0.025 about twice as that of the matrix. In comparison with the untreated one, the AZ91D alloy after CS-SP treatment showed the lower COF and the enhanced wear resistance. |