Study on treatment of printing and dyeing waste gas in the atmosphere with Ce-Mn/GF catalyst
| Autor: | Jianqi Liu, Xin Liu, Jiayao Chen, Chengyu Ma, F. C. Zhong |
|---|---|
| Rok vydání: | 2021 |
| Předmět: |
Materials science
010504 meteorology & atmospheric sciences Glass fiber Oxide Catalytic combustion 010502 geochemistry & geophysics 01 natural sciences Amorphous solid Catalysis Metal Polyester chemistry.chemical_compound Chemical engineering chemistry visual_art Specific surface area visual_art.visual_art_medium General Earth and Planetary Sciences 0105 earth and related environmental sciences General Environmental Science |
| Zdroj: | Arabian Journal of Geosciences. 14 |
| ISSN: | 1866-7538 1866-7511 |
| DOI: | 10.1007/s12517-021-07074-7 |
| Popis: | Glass fiber (GF) was selected as catalyst carrier, and the experiment was carried out to modify the glass fiber without catalyst carrier, so that it could achieve the best loading effect. The activity of the waste gas from the catalytic combustion of polyester cotton with Ce-Mn/GF series of catalysts decreased in the following order: Ce-Mn/GF (1:5), Ce-Mn/GF (1:4), Ce-Mn/GF (1:6), Ce-Mn/GF (1:3), and Ce-Mn/GF (1:2) (Ce/Mn ratio is molar ratio). When O2 concentration was less than 6%, O2 had a great influence on the reaction and is the main control factor of the reaction. However, when O2 concentration was higher than 6%, the influence of O2 concentration could be basically ignored, and the gas condition of the reaction became the main influence factor of the reaction. The activity of the catalyst was related to its specific surface area and pore structure. The specific surface area of the catalyst was affected by the loading capacity of metal oxide CeO2 and MnOx. The catalysts of Ce-Mn/GF (x) series (x ≠ 0), Mn existed in the state of Mn4+. The active centers CeO2 and MnOx are amorphous and uniformly dispersed on the carrier glass fiber. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full text from SpringerLink