Structural and optical properties of ZnO–SnO2 mixed thin films deposited by spray pyrolysis

Autor: T. Tharsika, A.S.M.A. Haseeb, Mohd Faizul Mohd Sabri
Rok vydání: 2014
Předmět:
Zdroj: Thin Solid Films. 558:283-288
ISSN: 0040-6090
DOI: 10.1016/j.tsf.2014.02.022
Popis: Nanocrystalline ZnO–SnO 2 mixed thin films were deposited by the spray pyrolysis technique at various substrate temperatures during deposition. The mixed films were prepared in the range of 20.9 at.% to 73.4 at.% by altering the Zn/(Sn + Zn) atomic ratio in the starting solution. Morphology, crystal structures, and optical properties of the films were characterized by field-emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), and ultraviolet–visible and photoluminescence (PL) spectroscopy. XRD analysis reveals that the crystallinity of the Sn-rich mixed thin films increases with increasing substrate temperatures. FESEM images show that the grain size of mixed thin films is smaller compared to that of pure ZnO and SnO 2 thin films. A drop in the thickness and optical bandgap of the film was observed for films fabricated at high temperatures, which coincided with the increased crystallinity of the films. The average optical transmission of mixed thin films increased from 70% to 95% within the visible range (400–800 nm) as the substrate temperature increases. Optical bandgap of the films was determined to be in the range of 3.21–3.96 eV. The blue shift in the PL spectra from the films was supported by the fact that grain size of the mixed thin films is much smaller than that of the pure ZnO and SnO 2 thin films. Due to the improved transmission and reduced grain size, the ZnO–SnO 2 mixed thin films can have potential use in photovoltaic and gas sensing applications.
Databáze: OpenAIRE
Externí odkaz: