Summary A new resin system, in which liquefied wood was reacted with various epoxy compounds, was previously developed. This paper reports the syntheses of two types of liquefied wood/epoxy resins with the ratio of liquefied wood to epoxy compounds (L/E ratio) of either 1/0.5 or 1/1. Furthermore, the viscoelastic properties obtained from the dynamic mechanical measurements of the cured resins and their adhesive bond properties measured as tensile shear strength are reported. The results from dynamic mechanical measurements indicated that the resins with a L/E ratio of 1/0.5 could be cured at 90°C, while the resins with L/E ratio of 1/1 were cured at 150°C. The resins cured with triethylene tetramine (TETA) at 150°C or 90°C had almost the same level of the normal adhesive shear strength as that of the commercial epoxy resin. The high level of adhesive shear strength of the resin cured at 150°C was maintained after the glued specimens were soaked in water at 60°C, while the share strength of the resins cured at 90°C was reduced by either the water soaking at 60°C or the cyclic boiling test. |