Damage Behavior in Simulated Service Environment of Thermal Control Oxidation Film of 2A12 Alloy
Autor: | Xu Guang Wang, Xue Zheng Yao, Qing Xin Cui, Chen Wen, Li Gong Zhang, Jia Feng Li, Jing Ying Bai |
---|---|
Rok vydání: | 2021 |
Předmět: |
010302 applied physics
Materials science Scanning electron microscope Mechanical Engineering Alloy chemistry.chemical_element Humidity 02 engineering and technology engineering.material 021001 nanoscience & nanotechnology 01 natural sciences Exfoliation joint Thermal control law.invention Cracking Optical microscope chemistry Mechanics of Materials law Aluminium 0103 physical sciences engineering General Materials Science Composite material 0210 nano-technology |
Zdroj: | Key Engineering Materials. 891:23-28 |
ISSN: | 1662-9795 |
DOI: | 10.4028/www.scientific.net/kem.891.23 |
Popis: | In order to obtain the service performance of the black anodic oxidation film of 2A12 aluminum alloy, the influence of humidity and temperature in storage environment and heat on the performance of black oxidation film were studied. And the morphologies were analyzed by using optical microscopy (OM) and scanning electron microscopy (SEM). The results showed that after the black anodic oxidation film is produced, "aging" will occur in the natural environment, which can lead to the structure change of the sealing pore and affect the service performance of the film. The film exfoliates off slightly under the humidity of 90%, and the film exfoliates off more seriously when the humidity over 95%. The temperature has a greater influence on the film cracking, especially when the temperature is above 120°C, it is easy to exfoliate off. The exfoliation model was established and the affection mechanism was discussed. |
Databáze: | OpenAIRE |
Externí odkaz: |