Evolution of weld metals nanostructure and properties under irradiation and recovery annealing of VVER-type reactors

Autor: Ya. I. Shtrombakh, S.V. Fedotova, Evgenia Kuleshova, O. O. Zabusov, D. A. Zhurko, B. A. Gurovich, K. E. Prikhod’ko
Rok vydání: 2013
Předmět:
Zdroj: Journal of Nuclear Materials. 434:72-84
ISSN: 0022-3115
DOI: 10.1016/j.jnucmat.2012.11.026
Popis: The results of VVER-440 steel Sv-10KhMFT and VVER-1000 steel SV-10KhGNMAA investigations by transmission electron microscopy, scanning electron microscopy, Auger-electron spectroscopy and mechanical tests are presented in this paper. The both types of weld metals with different content of impurities and alloying elements were studied after irradiations to fast neutron (E > 0.5 MeV) fluences in the wide range below and beyond the design values, after recovery annealing procedures and after re-irradiation following the annealing. The distinctive features of embrittlement kinetics of VVER-440 and VVER-1000 RPV weld metals conditioned by their chemical composition differences were investigated. It is shown that the main contribution into radiation strengthening within the design fluence can be attributed to radiation-induced precipitates, on reaching the design or beyond design values of fast neutron fluencies the main contribution into VVER-440 welds strengthening is made by radiation-induced dislocation loops, and in case of VVER-1000 welds – radiation-induced precipitates and grain-boundary phosphorous segregations. Recovery annealing of VVER-440 welds at 475 °C during 100 h causes irradiation-induced defects disappearance, transformation of copper enriched precipitates into bigger copper-rich precipitates with lower number density and leads to almost full recovery of mechanical properties followed by comparatively slow re-embrittlement rate. The recovery annealing temperature of VVER-1000 welds was higher – 565 °C during 100 h – to avoid temper brittleness. The annealing of VVER-1000 welds leads to almost full recovery of mechanical properties due to irradiation-induced defects disappearance and decrease in precipitates number density and grain-boundary segregation of phosphorus. The re-embrittlement rate of VVER-1000 weld during subsequent re-irradiation is at least not higher than the initial rate.
Databáze: OpenAIRE
Externí odkaz: