Low temperature Cathodoluminescence Studies of Tm and Er implanted hexagonal ZnS and ZnSe crystals

Autor: K. J. Howlett, A. D. Yoffe
Rok vydání: 1986
Předmět:
Zdroj: Zeitschrift f�r anorganische und allgemeine Chemie. 540:281-290
ISSN: 1521-3749
0044-2313
DOI: 10.1002/zaac.19865400931
Popis: Sharp line cathodoluminescence spectra were obtained at 8 K from Tm3+ and Er3+ ions implanted into hexagonal ZnS and ZnSe crystal platelets after annealing the implanted crystals for two hours at 500°C in vacuo. No rare earth emission was detected from ion implanted hexagonal CdS. Assignments have been made for the 2S+1LJ terms of the rare earth ions which were responsible for the observed luminescence. Although the lattice location of the ions may be considered, it is not at present possible for us to arrive at firm conclusions about their site symmetry since the spectra were too complex to permit a detailed crystal field analysis. Tieftemperatur-Kathodolumineszenz-Untersuchungen Von Tm- und Er-implantierten hexagonalen ZnS- und ZnSe-Kristallen Scharflinien-Kathodolumineszenzspektren wurden bei 8 K Von Tm3+-und Er3+-Ionen implantierten hexagonalen ZnS- und ZnSe-Plattchen Erhalten nach Temperung der implantierten Kristalle fur zwei Stunden bei 500°C im Vakuum. Beim ionenimplantierten hexagonalen CdS wurde keine Seltenen Erd-Emission beobachtet. Zuordnungen werden fur die 2S+1LJ-Terme der Seltenen Erd-Ionen gegeben, die fur die beobachtete Lumineszenz verantwortlich sind. Obgleich die Gitterplatze der Ionen dafur in Betracht kommen, ist es fur uns zur Zeit nicht moglich, abschliesende Aussagen uber ihre Zentrensymmetrie zu Erhalten, da die Spektren zu komplex sind, um eine Detaillierte Kristallfeldanalyse zu erlauben.
Databáze: OpenAIRE
Externí odkaz: