Stress relaxation of compacted graphite iron alloyed with molybdenum

Autor:	Vasile-Lucian Diaconu, Peter Skoglund, Torsten Sjögren, Attila Diószegi
Rok vydání:	2013
Předmět:	Materials science Compacted graphite iron Mechanical Engineering Metallurgy Metals and Alloys Fatigue testing chemistry.chemical_element Temperature cycling engineering.material Compressive strength chemistry Mechanics of Materials Molybdenum engineering Stress relaxation Cast iron Graphite
Zdroj:	International Journal of Cast Metals Research. 26:51-57
ISSN:	1743-1336 1364-0461
DOI:	10.1179/1743133612y.0000000036
Popis:	In a previous study, the thermomechanical fatigue resistance of four compacted graphite irons (CGIs) and one grey cast iron was investigated. The molybdenum content of the four CGIs varied between 0 and 1·01 wt-%. It was observed that during thermal cycling, the maximum value of the compressive stress continuously decreased while the value of the maximum tensile stress continuously increased. The continuous decrease in compressive stresses showed that stress relaxation occurs at elevated temperatures during thermal cycling. The goal of the present investigation was to investigate the phenomenon of stress relaxation at elevated temperatures. The tests were performed at 350 and 600°C respectively. The results of the stress relaxation tests performed at 600°C showed the same trend observed at thermomechanical fatigue testing. The tests showed that additions of molybdenum improved the fatigue resistance of CGI by lowering the stress relaxation rate.
Databáze:	OpenAIRE
Externí odkaz:	https://explore.openaire.eu/search/publication?articleId=doi_________::9d12f2483a61884b48ad75533b66789c https://doi.org/10.1179/1743133612y.0000000036 Zobrazit plný text záznamu Plný text ve formátu PDF Plný text ve formátu HTML
Nepřihlášeným uživatelům se plný text nezobrazuje	K zobrazení výsledku je třeba se přihlásit.