Butane/Propane Gas Sensing Using Zinc Oxide Film Grown by Successive Ionic Layer Adhesion and Reaction
| Autor: | Emmanuel A. Florido, Sarah Allyssa Solidum |
|---|---|
| Rok vydání: | 2016 |
| Předmět: |
Scanning electron microscope
Mechanical Engineering 010401 analytical chemistry Inorganic chemistry Analytical chemistry chemistry.chemical_element 020206 networking & telecommunications Butane 02 engineering and technology Zinc 01 natural sciences 0104 chemical sciences chemistry.chemical_compound Adsorption chemistry Volume (thermodynamics) Mechanics of Materials 0202 electrical engineering electronic engineering information engineering General Materials Science Nanorod Sodium zincate Wurtzite crystal structure |
| Zdroj: | Key Engineering Materials. 705:273-277 |
| ISSN: | 1662-9795 |
| Popis: | This study was aimed to test the ability of zinc oxide (ZnO) film fabricated by successive ionic layer adsorption and reaction (SILAR) to detect liquid petroleum gas consisting of a mixture of butane/propane gas. The film was fabricated by alternate dipping of pre-cleaned glass substrates in a sodium zincate bath and in a 95°C hot water bath using an automated dipping machine to control the sequence and dipping time. Scanning electron microscopy (SEM) revealed a uniform film consisting of wurtzite ZnO nanorods for the sample grown using 0.1M concentration of sodium zincate and 200 dippings. Current-voltage characterization of the samples showed an average resistivity of 1.343 Ω-m. EDS analysis of the film confirmed the existence of zinc oxide with 65.9% zinc and 34.1% oxygen. The ZnO film exhibited an ability to detect the gas with an average gas response of 0.44, average response time of 14 seconds and average recovery time of 25 seconds using a gas concentration in air of 1.5 % by volume. Response time is the time for the sensor to reach the peak voltage output from the start of gas exposure while recovery time is the time for the voltage output to return to the initial value without gas when the gas is removed from the chamber. The zinc oxide film also showed a voltage output of 100, 109.31, 118.92, 123.61, 133.5, and 149.52 mV when exposed to percent volume gas concentrations of 0, 0.5, 0.75, 1.0, 1.25, and 1.5, respectively with a correlation coefficient of 0.97. The sensor sensitivity is 32 Δ(mV)/Δ(%conc). |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|