In Situ Observation on Lime Dissolution in Molten Metallurgical Slags – Kinetic Aspects
| Autor: | Zhi Sun, Muxing Guo, Xiaoling Guo, Bart Blanpain, J. Van Dyck |
|---|---|
| Rok vydání: | 2014 |
| Předmět: |
Materials science
General Chemical Engineering Diffusion Metallurgy Slag General Chemistry Atmospheric temperature range engineering.material Chemical reaction Industrial and Manufacturing Engineering Boundary layer visual_art engineering visual_art.visual_art_medium Layer (electronics) Dissolution Lime |
| Zdroj: | Industrial & Engineering Chemistry Research. 53:6325-6333 |
| ISSN: | 1520-5045 0888-5885 |
| DOI: | 10.1021/ie500070h |
| Popis: | The chemical dissolution of lime particles in molten CaO–Al2O3–SiO2-based slags was observed by using a confocal scanning laser microscope (CSLM) in a temperature range from 1450 to 1600 °C. The dissolution behavior was found to be largely dependent on temperature and slag chemistry. A considerable increase in the dissolution rate was observed at elevated temperatures. The in situ observations revealed that the dissolution process in the slags containing MgO was controlled by chemical reactions at the interface. For slags without MgO, the dissolution could be divided into three stages when an interfacial reaction (IR) layer formed at the interface. The dissolution was limited by chemical reactions during the early stage, a mixed control of product layer and boundary layer diffusion during the intermediate stage, and boundary layer diffusion control in the final stage. The IR layer formed during dissolution at the interface between the lime particles, and the liquid slag free of MgO was clearly a kinetic b... |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|