A Study of La(Mn1−xNix)O3 and Its Bonding with Cubic ZrO2

Autor: Kyuya Narita, Jun-ichi Echigoya
Rok vydání: 1990
Předmět:
Zdroj: physica status solidi (a). 122:87-95
ISSN: 1521-396X
0031-8965
DOI: 10.1002/pssa.2211220108
Popis: A series of solid solutions of the La(Mn1−xNix)O3 system is prepared and investigated by X-ray diffraction, electron diffraction, electrical resistivity, and thermal expansion coefficient measurement. Finding shows that a complete range of solid solution exists with face centered cubic structure. The electrical resistivities of La(Mn1−xNix)O3 are quite low in the order of 10−2 Ω cm at 1173 K. The thermal expansion coefficient has a minimum at a composition around x = 0.4 and had the same value as that of 10 mol1% Y2O3ZrO2 at a composition of x = 0.2. The bonding of La(Mn1−xNix)O3 (x = 0.2) with cubic ZrO2 is achievied at 1573 K under a pressure of 2 MPa for 127.8 ks. The high resolution TEM image reveals that both phases are bonded directly without any cracks or third phases at the interface. Eine Reihe von Mischkristallen des La(Mn1−xNix)O3-Systems wird prapariert und mittels Rontgenbeugung, Elektronenbeugung und Messungen des elektrischen Widerstands und des thermischen Ausdehnungskoeffizienten untersucht. Die Ergebnisse zeigen, das ein kompletter Bereich von Mischkristallen mit kubisch-flachenzentrierter Struktur existiert. Die elektrischen Widerstande von La(Mn1−xNix)O3 sind ziemlich niedrig von der Grosenordnung 10−2 ω cm bei 1173 K. Der thermische Ausdehnungskoeffizient besitzt ein Minimum bei einer Zusammensetzung von etwa x = 0.4 und hat denselben Wert wie der von 10 Mol% Y2O3ZrO2 bei einer Zusammensetzung von x = 0,2. Die Verbindung von La(Mn1−xNix)O3 (x = 0,2) mit kubischem ZrO2 wird bei 1573 K unter einem Druck von 2 MPa fur 127,8 ks erreicht. Das Hochauflosungs-TEM-Diagramm zeigt, das beide Phasen direkt verbunden werden ohne irgendwelche Risse oder dritte Phasen an der Grenzflache.
Databáze: OpenAIRE
Externí odkaz: