Kinetically stable Pt x Ir 100-x alloy thin films prepared by pulsed laser deposition: Oxidation of NH 3 and poisoning resistance
| Autor: | David A. Finkelstein, Daniel Guay, Régis Imbeault, Sébastien Garbarino, David Reyter, Lionel Roué |
|---|---|
| Rok vydání: | 2014 |
| Předmět: |
Materials science
General Chemical Engineering Alloy Analytical chemistry chemistry.chemical_element 02 engineering and technology engineering.material 010402 general chemistry 021001 nanoscience & nanotechnology 01 natural sciences 0104 chemical sciences Pulsed laser deposition X-ray photoelectron spectroscopy chemistry Electrochemistry engineering Crystallite Iridium Thin film 0210 nano-technology Platinum Solid solution |
| Zdroj: | Electrochimica Acta. 142:289-298 |
| ISSN: | 0013-4686 |
| Popis: | A series of kinetically stable Pt x Ir 100-x thin film alloys have been synthesized by crossed beam pulsed laser deposition and physically characterized by X-ray diffraction and X-ray photoelectron spectroscopy. It is shown that a metastable solid solution between Pt and Ir is formed over the whole composition range, with the lattice parameter of the fcc phase increasing steadily between 3.84 and 3.92 A as the Pt content is increased from 0 to 100 at.%. The surface composition of all samples follows closely the bulk composition, indicating there is no surface segregation of either element. A detailed analysis of the Pt and Ir 4f core level peaks shows that the binding energy of the Pt 4f 7/2 and Ir 4f 7/2 core level peaks both decrease with increasing Pt concentration, from 71.6 to 71.2 eV as the bulk Pt content increases from ca 65% to 100%, and from 61.1 to 60.6 eV as the bulk Pt content increases from 0 to 90 at.%, respectively. Such behaviour was recently shown to reflect a change in the center of gravity of the occupied states, where the d-band level of both Pt and Ir shift to higher energy as the Pt bulk content is decreased. Both the surface composition and surface electronic structure are not altered following all the electrochemical analyses. The electrocatalytic properties of these Pt x It 100-x alloys for the anodic oxidation of NH 3 in aqueous alkaline media were investigated. Voltammetric and chronoamperometric studies on these alloys show improved poison tolerance for NH 3 oxidation as compared to pure polycrystalline platinum, with optimal results observed with Pt 89 Ir 11 alloys. Such improvement for long term stability is associated with the electronic effect and bifunctional mechanism at the PtIr surface alloys. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect