Removal of residual stresses by low-temperature annealing to prevent stress-corrosion cracking of carbon steels
| Autor: | G. V. Karpenko, A. I. Zyubrik, I. I. Vasilenko, N. N. Zhagalyak |
|---|---|
| Rok vydání: | 1972 |
| Předmět: |
Materials science
Carbon steel Environmental stress cracking Annealing (metallurgy) Mechanical Engineering Metallurgy technology industry and agriculture engineering.material Intergranular corrosion Condensed Matter Physics Cracking Mechanics of Materials Residual stress Boiling engineering General Materials Science Composite material Stress corrosion cracking |
| Zdroj: | Soviet Materials Science. 5:312-317 |
| ISSN: | 1573-885X 0038-5565 |
| Popis: | The effect of low-temperature annealing on the relaxation of residual stresses and on the stress-corrosion resistance of carbon steels was investigated. It was shown that stress-corrosion cracking of welded joints in carbon steels under the influence of boiling nitrate solutions and alkaline solutions is prevented by annealing at temperatures ≥450° C and ≥500° C, respectively. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full text from SpringerLink