| Popis: |
The synthesis of ceramic materials in the Zn2SiO4‒RO (R ― Ba, Sr)‒Al2O3‒SiO2 system was carried out using the technology of exothermic synthesis from solutions including zinc, barium and strontium nitrates, silica and organic reducing agent (glycine and carbamide). It is shown that the implementation of an exothermic process followed by calcination at a temperature of 1000 °C contributes to the formation of crystalline phases of willemite (Zn2SiO4), barium aluminosilicates (BaAl2Si2O8) and strontium (SrAl2Si2O8). The dependence of the quantitative phase composition and parameters of the elementary cells of the crystalline phases is established. Sintering of synthesized materials occurs at a temperature of 1275 °C. The dielectric permittivity of sintered materials is 5,33‒6,06 and the tangent of the dielectric loss angle is 1,5·10‒3‒3,16·10‒3 at a frequency of 1 MHz, the minimum values correspond to ceramics based on the Zn2SiO4‒BaAl2Si2O8‒SrAl2Si2O8 triple system. Ill. 5. Ref. 19. Tab. 2. |