Formation of {001} <510> recrystallization texture and magnetic property in strip casting non-oriented electrical steel
Autor: | Li Chenggang, Sang-Hoon Kim, Byung-Deug Hong, Yu Sun, Yi-qing Qiu, Zhenyu Liu, Guodong Wang, Cao Guangming, Hai-Tao Liu |
---|---|
Rok vydání: | 2012 |
Předmět: |
Materials science
Annealing (metallurgy) Mechanical Engineering Metallurgy Nucleation Recrystallization (metallurgy) engineering.material Condensed Matter Physics Grain growth Strip casting Mechanics of Materials engineering Dynamic recrystallization General Materials Science Grain boundary migration Electrical steel |
Zdroj: | Materials Letters. 81:65-68 |
ISSN: | 0167-577X |
Popis: | A 3.2 wt.%Si–0.7 wt.%Al non-oriented silicon steel as-cast sheet with developed columnar grains and λ-fiber ( ∥ ND) texture was produced by twin-roll strip casting process, and subsequently treated with cold rolling and annealing. Texture evolution at each condition was investigated using macro-/microtexture analysis. It was shown that the cold rolled sheet was characterized by pronounced {001} ~{115} fiber and quite weak γ-fiber ( ∥ ND) texture. After annealing, the recrystallization texture was dominated by desirable λ-fiber with a peak at {001} together with extremely weak γ-fiber, and consequently the magnetic induction was significantly improved. It was indicated that the formation of {001} recrystallization texture could be attributed to the preferred nucleation and grain growth by the strain-induced grain boundary migration (SIBM) mechanism. |
Databáze: | OpenAIRE |
Externí odkaz: |