| Autor: |
Ahmad Hakimi Shaffie, A.S.A. Khiar |
| Rok vydání: |
2018 |
| Předmět: |
|
| Zdroj: |
AIP Conference Proceedings. |
| ISSN: |
0094-243X |
| DOI: |
10.1063/1.5041232 |
| Popis: |
Polymer electrolyte is an ionic conductor formed by dissolving salt in polymer host. In this work, starch/chitosan blend based polymer electrolyte was prepared with different weight percentage of Ammonium Nitrate (NH4NO3) via solution casting technique. The film was characterized by impedance spectroscopy HIOKI 3531- 01 LCR Hi-Tester to measure its ionic conductivity over a wide range of frequency between 50Hz-5MHz and at ambient temperature. Sample with 35 wt% of NH4NO3 shows the highest conductivity of (6.34 ± 1.52) = 10−7 Scm-1. X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy were used to correlate the ionic conductivity results.Polymer electrolyte is an ionic conductor formed by dissolving salt in polymer host. In this work, starch/chitosan blend based polymer electrolyte was prepared with different weight percentage of Ammonium Nitrate (NH4NO3) via solution casting technique. The film was characterized by impedance spectroscopy HIOKI 3531- 01 LCR Hi-Tester to measure its ionic conductivity over a wide range of frequency between 50Hz-5MHz and at ambient temperature. Sample with 35 wt% of NH4NO3 shows the highest conductivity of (6.34 ± 1.52) = 10−7 Scm-1. X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy were used to correlate the ionic conductivity results. |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|