| Autor: |
A. J. Panson, Aleksander I. Braginski, J. R. Gavaler, John K. Hulm, H. C. Pohl, J. Talvacchio, A. M. Stewart, M.A. Janocko, G. R. Wagner |
| Rok vydání: |
1987 |
| Předmět: |
|
| Zdroj: |
Physical Review B. 35:8774-8777 |
| ISSN: |
0163-1829 |
| Popis: |
Changes in the ratios of cations by \ensuremath{\sim}10% off the ${\mathrm{Y}}_{1}$${\mathrm{Ba}}_{2}$${\mathrm{Cu}}_{3}$${\mathrm{O}}_{8\mathrm{\ensuremath{-}}\mathrm{y}}$ composition demonstrated that a range of solid solutions exists in this material. The critical temperature within this range is strongly composition dependent and falls off from above 90 K to \ensuremath{\sim}70 K. Annealing stoichiometric samples in 1 bar of oxygen at 700 \ifmmode^\circ\else\textdegree\fi{}C for 36 and 108 h resulted in narrowing of the magnetic susceptibility transition and significant increases in the critical current density ${J}_{c}$, p-type effective carrier concentration ${n}^{\mathrm{*}}$, and upper critical field, ${H}_{c2}$. After annealing, ${J}_{c}$ between 5 and 60 kOe was (3--1.5)\ifmmode\times\else\texttimes\fi{}${10}^{4}$ A/${\mathrm{cm}}^{2}$ at 4.2 K and (2--0.5)\ifmmode\times\else\texttimes\fi{}${10}^{2}$ A/${\mathrm{cm}}^{2}$ at 77 K. The value of ${n}^{\mathrm{*}}$ after annealing was 4.2\ifmmode\times\else\texttimes\fi{}${10}^{21}$ ${\mathrm{cm}}^{\mathrm{\ensuremath{-}}3}$. An extrapolated value of ${H}_{c2}$(T=0)=1.2 MOe was obtained from \ensuremath{\Vert}${\mathrm{dH}}_{c2}$/dT\ensuremath{\Vert}=19 kOe/K. A set of microscopic superconducting parameters was derived from results of resistive measurements made on a single, annealed specimen. |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|