Effects of MgO on dielectric properties and electrical conductivity of ternary zinc magnesium phosphate glasses

Autor: S. F. Khor, H.A.A. Sidek, Zainal Abidin Talib, W. M. Daud, B. H. Ng
Rok vydání: 2009
Předmět:
Zdroj: Journal of Non-Crystalline Solids. 355:2533-2539
ISSN: 0022-3093
DOI: 10.1016/j.jnoncrysol.2009.09.010
Popis: Glasses with composition ( ZnO ) 30 ( MgO ) x ( P 2 O 5 ) 70 - x (x = 5, 8, 13, 18 and 20 mol%) have been successfully prepared by the melt-quenching technique. The dielectric permittivity ( e ′ ) and loss factor ( e ″ ) were measured in the frequency range of 0.01 Hz to 1 MHz and in the temperature range of 303 to 573 K. From the results, there is evidence of dipolar relaxation occurring between 10 3 – 10 6 Hz , while at low frequencies, the spectrum is dominated by dc conduction which was manifested by the 1 / ω slope of the loss factor plot. The value of the relaxing frequency ( ω p ) plotted against 1 / T shows a single relaxation mechanism with an activation energy of 0.45 eV. The average value of the activation energy for dc conduction was much higher (1.25 eV) suggesting its diffusion movement had encountered more difficult steps than the small displacement changing dipoles. With increasing MgO concentration, the dielectric permittivity ( e ′ ), dc conductivity ( σ dc ) and dielectric strength ( Δ e ) decrease and these were attributed to some of the magnesium ions participated in the glass-forming positions as well as modifiers. At lower temperatures, the complex permittivity plots present a skewed arc with center point lying below the real axis which is a non-Debye characteristic. The empirical data were sufficiently fitted by using the Harviliak–Negami equation. The temperature dependent of the parameter α is discussed.
Databáze: OpenAIRE
Externí odkaz: