Control of carrier concentration of p-type transparent conducting CuScO2(0001) epitaxial films
| Autor: | Atsushi Ashida, Norifumi Fujimura, Yoshiharu Kakehi, Takeshi Yoshimura, Kazuo Satoh |
|---|---|
| Rok vydání: | 2010 |
| Předmět: |
Chemistry
Band gap Metals and Alloys Analytical chemistry Mineralogy Surfaces and Interfaces Activation energy Epitaxy Surfaces Coatings and Films Electronic Optical and Magnetic Materials Electrical transport Electrical resistivity and conductivity Materials Chemistry Sapphire Excess oxygen Electrical conductor |
| Zdroj: | Thin Solid Films. 518:3097-3100 |
| ISSN: | 0040-6090 |
| DOI: | 10.1016/j.tsf.2009.07.204 |
| Popis: | Excess oxygen and 1-at% Mg co-doped CuScO 2 [3R](0001) epitaxial films were prepared on a-plane sapphire substrates by combining two-step deposition and post-annealing techniques. The optical and electrical transport properties of the co-doped epitaxial films were compared with those of the CuScO 2 [3R](0001) epitaxial films. No significant increase in optical absorption was observed in the co-doped epitaxial films, and the energy gap for direct allowed transition was estimated at 3.7 eV. The carrier concentration of CuScO 2 [3R](0001) epitaxial films was controlled from ~ 10 16 cm - 3 to ~ 10 18 cm - 3 at room temperature by adjusting the excess oxygen and Mg co-doping. The electrical conductivity, carrier concentration, and Hall mobility of the most conductive film were 3.6 × 10 - 2 Scm - 1 , 8.5 × 10 17 cm - 3 and 2.6 × 10 - 1 cm 2 V - 1 s - 1 at room temperature, respectively. The temperature dependence of the electrical transport properties of the film exhibited semiconducting characteristics, and the activation energy estimated from the temperature dependence of the carrier concentration was 0.50 eV. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect