Chemical solution deposition of YBa2Cu3O7−x films by dip coating
| Autor: | Brigitte Schlobach, Bernhard Holzapfel, Martina Falter, Wolfgang Häßler |
|---|---|
| Rok vydání: | 2002 |
| Předmět: |
Superconductivity
Materials science Annealing (metallurgy) Analytical chemistry Energy Engineering and Power Technology chemistry.chemical_element Condensed Matter Physics Epitaxy Oxygen Nitrogen Dip-coating Electronic Optical and Magnetic Materials chemistry.chemical_compound chemistry Strontium titanate Electrical and Electronic Engineering Thin film |
| Zdroj: | Physica C: Superconductivity. :46-49 |
| ISSN: | 0921-4534 |
| DOI: | 10.1016/s0921-4534(02)00738-4 |
| Popis: | Dense superconducting YBa 2 Cu 3 O 7− x (YBCO) films were prepared via chemical solution deposition in a trifluoroacetate (TFA) process. The dip coated substrates were treated in a two stage annealing process under wet oxygen below 400 °C and subsequently heated up to 800 °C in a wet nitrogen dominated atmosphere. We obtained epitaxially grown 190 nm thick films on single-crystalline strontium titanate with T c of 89.9 K and a transition width of 0.7 K. Critical current densities up to 2.7 MA cm −2 were reached. YBCO layers up to 400 nm thickness can be processed without forming cracks during the heating treatment. Biaxially textured strontium titanate films and ytterbium oxide films as buffer layers were also built in a TFA process on single-crystalline substrates. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect