Autor: Rudolf Schmolke, Burkhard Schulz, Eberhard Leibnitz, Dieter Hofmann
Rok vydání: 1993
Předmět:
Zdroj: Angewandte Makromolekulare Chemie. 204:111-118
ISSN: 1522-9505
0003-3146
DOI: 10.1002/apmc.1993.052040110
Popis: Depending on the coagulation conditions, poly(p-phenylene-1,3,4-oxadiazole) in the solid state forms two modifications, as can be evidenced by FTIR spectroscopy and by wide-angle X-ray scattering curves (WAXS). In both cases each modification is detectable by characteristic peaks. Processing of fibers or films from solutions in concentrated sulfuric acid by coagulation in water results in the formation of a thermodynamically non-equilibrium form, defined as β-modification. Under special conditions it is possible to obtain the three-dimensionally ordered equilibrium α-structure that leads to processing products with markedly higher tenacities. Abhangig von den Fallbedingungen tritt Poly(p-phenylen-1,3,4-oxadiazole) in zwei Modifikationen auf. Dies kann sowohl durch FTIR-Spektroskopie als auch mit Rontgenweitwinkelstreuung nachgewiesen werden. In beiden Fallen zeigt jede Modifikation charakteristische Peaks. Bei der Verarbeitung zu Faden oder Filmen aus Losungen in konzentrierter Schwefelaure durch Fallen in Wasser wird die im thermodynamischen Ungleichgweicht stehende β-Modifikation erhalten. Unter speziellen Bedingungen ist es moglich, die dreidimensional geordnete Gleichgewichtsstruktur direkt herzustellen. Verarbeitungsprodukte aus dieser α-Modifikation weisen merklich hohere Festigkeiten auf.
Databáze: OpenAIRE
Externí odkaz: