Fracture Failure Analysis of the Blowout Preventer Ram in an Oilfield
Autor: | Zhi Hai Fan, Nan Ji, Ke Tong, Dong Feng Li, Shen Cong |
---|---|
Rok vydání: | 2021 |
Předmět: |
010302 applied physics
Materials science Mechanical Engineering 02 engineering and technology 021001 nanoscience & nanotechnology Condensed Matter Physics 01 natural sciences Fracture failure Mechanics of Materials 0103 physical sciences General Materials Science Geotechnical engineering 0210 nano-technology Brittle fracture Blowout preventer |
Zdroj: | Materials Science Forum. 1035:458-463 |
ISSN: | 1662-9752 |
Popis: | This paper gives a thorough investigation on the fracture failure of the blowout preventer (BOP) ram. Through appearance inspection, magnetic powder inspection, physicochemical inspection, metallographic inspection and scanning electron microscope (SEM), the main fracture reason of the BOP ram is that there was some original cracks in the BOP ram before fracture, during the service process the bop ram is subjected to impact load, therefore brittle fracture occurs due to the high brittleness of the gate material (which is caused by large internal structure) and low anti-crack propagation ability. Key words: Blowout preventer (BOP) ram; Fatigue break; Brittle fracture; Failure analysis |
Databáze: | OpenAIRE |
Externí odkaz: |