Monitoring abiotic degradation of branched polyethylenes formulated with pro-oxidants through different mechanical tests
| Autor: | Alejandro J. Müller, Alejandro J. Benítez, Johan J. Sánchez, María Luisa Arnal |
|---|---|
| Rok vydání: | 2013 |
| Předmět: |
Materials science
Polymers and Plastics Polyethylene Weather exposure Condensed Matter Physics Accelerated aging Work of fracture chemistry.chemical_compound Abiotic degradation chemistry Mechanics of Materials Tearing Ultimate tensile strength Materials Chemistry Degradation (geology) Composite material |
| Zdroj: | Polymer Degradation and Stability. 98:1705-1716 |
| ISSN: | 0141-3910 |
| DOI: | 10.1016/j.polymdegradstab.2013.06.004 |
| Popis: | The mechanical properties of two linear low density and low density polyethylenes containing a pro-oxidant additive were monitored during accelerated aging (60 °C in a convection oven) and weather exposure. Tearing tests (trouser) were performed for the first time in polyethylenes subjected to oxo-degradation revealing a transition from an extensible to a non-extensible material, at exposure times when standard tensile tests were not able to detect any changes in the materials. The essential work of fracture (EWF) technique was also applied and the results were in agreement with those of trouser tests. The specific essential work of fracture first increased with exposure time until the sample experienced a transition to a less ductile state where EWF was no longer applicable. EWF and trouser tear tests were more sensitive detecting the onset of degradation probably because they employ notched specimens that impose more critical stress concentration conditions than conventional tensile tests. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect