Texture evolution behavior and anisotropy of 2A97 Al–Li alloy during recrystallization at elevated temperature
| Autor: | Yue Ma, Yong-Hong Yang, Dong Wang, Chong Gao, Hong-Yun Luo |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
Materials science
Condensed matter physics 020502 materials Alloy Metals and Alloys Recrystallization (metallurgy) 02 engineering and technology engineering.material 021001 nanoscience & nanotechnology Condensed Matter Physics 0205 materials engineering Metallic materials Materials Chemistry engineering Physical and Theoretical Chemistry 0210 nano-technology Anisotropy |
| Zdroj: | Rare Metals. |
| ISSN: | 1867-7185 1001-0521 |
| DOI: | 10.1007/s12598-018-0997-y |
| Popis: | 2A97 Al–Li alloy was cold-rolled to 2 mm and then thermally exposed at different temperatures for 1 h and at 723 K for different time, respectively. The texture evolution behavior and the anisotropy of 2A97 Al–Li alloy were investigated. The result shows that the {001} 〈120〉 and {011} 〈233〉 textures are the dominant recrystallization texture. The {124} 〈211〉 texture is the final recrystallization texture. In case of low-temperature thermal exposure (473, 573 K), the {011} 〈211〉 texture is aggregated to the {112} 〈111〉 and {123} 〈634〉 textures. During the recrystallization at 723 K, the {001} 〈110〉, {111} 〈112〉 and {011} 〈100〉 textures are the intermediate transition grain orientations. The concurrent precipitation of Al20Cu2Mn3 and Al3Zr results in the occurrence of unusually sharp {011} 〈233〉 and {001} 〈120〉 texture components during recrystallization. The alloy with both recrystallization and deformation texture possesses the smallest anisotropic, and the texture is the direct reason that results in the anisotropy. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full text from SpringerLink