CW Laser Annealed Small-Geometry NMOS Transistors

Autor: A. R. Boothroyd, A.A. Naem, I.D. Calder
Rok vydání: 1983
Předmět:
Zdroj: MRS Proceedings. 23
ISSN: 1946-4274
0272-9172
DOI: 10.1557/proc-23-229
Popis: Small geometry NMOS transistors were fabricated using junctions implanted with 1016; Asplus;/cm2; @ 180 keV and annealed through 1067 Å of SiO 2; with a cw argon laser. Phosphosilicate glass densification was the only other high temperature step. Channel lengths were varied from 1.3 to 50 μ. and channel widths from 1 to 50,μ. Physical characterization of these devices revealed a junction depth of 3000 Å with negligible lateral diffusion. The smallest transistor had approximately a square channel with WxL = 1×l.3μ2;. IDS;−VDS; characteristics of this device were similar to those of large geometry devices due to counteracting short and narrow channel effects. The threshold voltage was 0.61±0.013 V across an entire wafer, while there was no punch-through for VDS;DS; < 14 V. The junctions showed a forward-biased ideality factor of 1.17, and the contact resistance in an 8 × 8 μ2; area was 1.5Ω to the source/drain regions and 0.5Ω to laser-recrystallized polysilicon interconnects. It is concluded that cw laser annealing can be used to fabricate small-geometry devices with excellent performance and without any deleterious effects.
Databáze: OpenAIRE
Externí odkaz: