Effect of aging time on corrosion behavior of as-forged AZ80 magnesium alloy
| Autor: | Ruo-mei Liu, Hui-zhong Li, Xiaopeng Liang, Hui-juan Liao, Xiao-feng Zhou, Min Deng |
|---|---|
| Rok vydání: | 2015 |
| Předmět: |
Materials science
Metallurgy Alloy Metals and Alloys Potentiodynamic polarization chemistry.chemical_element engineering.material Geotechnical Engineering and Engineering Geology Condensed Matter Physics Corrosion chemistry Aluminium Volume fraction Materials Chemistry engineering Magnesium alloy Corrosion behavior Porosity |
| Zdroj: | Transactions of Nonferrous Metals Society of China. 25:3921-3927 |
| ISSN: | 1003-6326 |
| DOI: | 10.1016/s1003-6326(15)64039-0 |
| Popis: | The corrosion behaviors of an as-forged AZ80 magnesium alloy after aging treatment for various durations at 170 °C were investigated by immersion test, H2 evolution test, SEM and potentiodynamic polarization curve measurement. The results show that the corrosion rate of the alloy decreases dramatically with the increase of aging time during the initial aging stage, but increases slowly with the aging time longer than 20 h. The volume fraction of β-Mg17Al12 increases with aging time within the first 20 h, leading to the decrease of corrosion rate. After aging for longer than 39 h, the growth of β phase is accompanied by the consumption of aluminum in the matrix, resulting in an increase in the corrosion rate. When the volume fraction of β phase is low, specimens suffer from severe local corrosion, which results in a porous surface. On the contrary, when the volume fraction of β phase is high, specimens suffer uniform corrosion attack. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect