Water vapor concentration dependence and temperature dependence of Li mass loss from Li2TiO3 with excess Li and Li4SiO4
| Autor: | Hiroki Ushida, Ryotaro Yamamoto, Kazunari Katayama, Satoshi Fukada, Tsuyoshi Hoshino, Motoki Shimozori |
|---|---|
| Rok vydání: | 2015 |
| Předmět: |
Range (particle radiation)
Materials science Mechanical Engineering Vapour pressure of water Analytical chemistry Atmosphere Breeder (animal) Adsorption Nuclear Energy and Engineering visual_art Desorption visual_art.visual_art_medium General Materials Science Ceramic Water vapor Civil and Structural Engineering |
| Zdroj: | Fusion Engineering and Design. :1808-1811 |
| ISSN: | 0920-3796 |
| DOI: | 10.1016/j.fusengdes.2015.03.015 |
| Popis: | In this study, weight reduction of Li 2 TiO 3 with excess Li and Li 4 SiO 4 at elevated temperatures under hydrogen atmosphere or water vapor atmosphere was investigated. The Li mass loss for the Li 2 TiO 3 at 900 °C was 0.4 wt% under 1000 Pa H 2 atmosphere and 1.5 wt% under 50 Pa H 2 O atmosphere. The Li mass loss for the Li 2 TiO 3 increased proportionally to the water vapor pressure in the range from 50 to 200 Pa at 900 °C and increased with increasing temperature from 700 to 900 °C although Li mass loss at 600 °C was significantly smaller than expected. It was found that water vapor concentration dependence and temperature dependence of Li mass loss for the Li 2 TiO 3 and the Li 4 SiO 4 used in this work were quite different. Water vapor is released from the ceramic breeder materials into the purge gas due to desorption of adsorbed water and water formation reaction. The released water vapor possibly promotes Li mass loss with the formation of LiOH on the surface. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect