Analysis of Corrosion Causes in the Export of a Compressor in the Pipeline of Western China
| Autor: | Ke Tong, En Peng Song, Shen Cong, Ji Cheng Ren, Ting Ting Qu |
|---|---|
| Rok vydání: | 2020 |
| Předmět: |
010302 applied physics
Materials science Petroleum engineering Mechanical Engineering Pipeline (computing) 02 engineering and technology 021001 nanoscience & nanotechnology Condensed Matter Physics 01 natural sciences Corrosion Mechanics of Materials 0103 physical sciences General Materials Science 0210 nano-technology China Gas compressor |
| Zdroj: | Materials Science Forum. 993:1218-1223 |
| ISSN: | 1662-9752 |
| Popis: | The field investigation, macro-inspection, thickness measurement, chemical components examination, mechanical characters tests, microstructure, SEM, XRD analysis and soil composition test were carried out, in order to analysis the external corrosion of the L415 pipe line near the compressor outlet. The results showed that the frequent vibration of the compressor outlet could lead to the damage and failure of the anticorrosive layer, which made the steel pipe loses protection and further exposed to the external environment to cause oxygen corrosion. The content of Cl- in soil was higher in the western China, which accelerated the corrosion of pipe. The corrosion acceleration mainly depended on the pipeline temperature and the secondary external anticorrosive layer. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|