Preparation and Characterization of Silica Gel from Bagasse Ash
| Autor: | Surapong Chirarattananon, Chantana Punlek, Chanchira Channoy, Somchai Maneewan |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
010302 applied physics
Materials science Bagasse ash Silica gel Extraction (chemistry) General Engineering 02 engineering and technology 021001 nanoscience & nanotechnology 01 natural sciences Characterization (materials science) chemistry.chemical_compound chemistry 0103 physical sciences 0210 nano-technology Nuclear chemistry |
| Zdroj: | Advanced Materials Research. 1145:44-48 |
| ISSN: | 1662-8985 |
| DOI: | 10.4028/www.scientific.net/amr.1145.44 |
| Popis: | Sugarcane bagasse is an agricultural waste that is potentially used as natural silica resources. Natural silica claimed to be safe in handing, cheap and can be generate from cheap resource. In the objectives of this study were to prepared silica from Sugarcane bagasse. The preparation of Sugarcane bagasse ash by burning at 700 °C for 4 and 6 h, respectively in atmosphere. The result of X-ray florescent: XRF, silica content which was obtained after heat treatment at 700 °C for 6 h was 80.814 wt%. Bagasse ash was purified by alkaline extraction method with 1.5, 2 and 2.5 N sodium hydroxide (NaOH), respectively. And refluxed by using concentrated 2 N sulfuric acid. From X-ray diffraction pattern showed that the obtained products were amorphous silica, 2.5 N sodium hydroxide. The morphology was observed by SEM, sphere and average particles dimension of synthesis silica with 1.5, 2 and 2.5 N NaOH are 120, 100 and 80 nm respectively. The SEM micrographs showed that the Concentration of NaOH was increased, the particles dimension decreased |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|