JiaQi Zhu, Wei Liu, Banthukul Wongpat, Baojun Dong, Fei Wu, Tianyi Zhang, Yonggang Zhao, Yueming Fan |
| Rok vydání: |
2020 |
| Předmět: |
|
| Zdroj: |
Anti-Corrosion Methods and Materials. 67:166-177 |
| ISSN: |
0003-5599 |
| DOI: |
10.1108/acmm-06-2019-2147 |
| Popis: |
PurposeThe salinity of the oilfield produced water has a significant effect on steel corrosion. The purpose of this paper is to study the influence of salinity on corrosion behavior of X60 steel and it also provides basic for material selection of gas wells with high salinity.Design/methodology/approachThe weight loss experiment was carried out on steel with high temperature and high pressure autoclave. The surface morphology and composition of corrosion scales were studied by means of scanning electron microscopy, energy dispersive spectroscopy and X-ray diffractometry.FindingsThe results show that as salinity increases, the corrosion rate of X60 steel will gradually experience a rapid decline stage and then a slow decline stage. X60 steel is mainly exhibiting uniform corrosion in the first rapid decline stage and pitting corrosion in the second slow decline stage. The increase in salinity reduces gas solubility, which, in turn, changes the morphology and density of the corrosion scales of X60 steel. At low salinity, loose iron oxides generated on the surface of the steel, which poorly protects the substrate. At high salinity, surface of the steel gradually forms protective films. Chloride ions in the saline solution mainly affect the structure of the corrosion scales and initiate pitting corrosion. The increased chloride ions lead to more pitting pits on the surface of steel. The recrystallization of FeCO3in pitting pits causes the corrosion scales to bulge.Originality/valueThe investigation determined the critical concentration of pitting corrosion and uniform corrosion of X60 steel, and the new corrosion mechanism model was presented. |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|