Thermal decomposition of poly(tetramethyloxydisilaethylene)

Autor: Jan Kurjata, Martel Zeldin, S. Rubinsztajn, Julian Chojnowski, M. Scibiorek
Rok vydání: 1992
Předmět:
Zdroj: Journal of Inorganic and Organometallic Polymers. 2:387-404
ISSN: 1572-8870
1053-0495
DOI: 10.1007/bf00701113
Popis: Thermal decomposition of poly[oxybis(dimethylsilylene)] having chains terminated with trimethylsiloxy groups was studied by thermogravimetry, pyrolysis-mass spectrometry, and infrared spectroscopy. The polymer is thermally less stable than poly(dimethylsiloxane). Depolymerization occurs at temperatures of 250–350°C, although this process also takes place at lower temperatures. The depolymerization produces cyclic oligomers of general formula [(Me2Si)2O] n , with predominant formation of the oligomern=2. The depolymerization is accompanied by processes which are referred to as restructurization because they change the structure of the polymer backbone. Decomposition may lead also to the formation of branching points. The shape of the thermograms taken under isothermal conditions is in agreement with an unzipping mechanism for depolymerization involving random initiation. Excluding the short initial period of the process, the unzipping is terminated at a restructurization point. A low activation energy points to initiation induced by electron transfer, presumably involving traces of contaminant. At higher temperatures, 350–600°C, loss of organic parts of the polymer takes place along with further restructurization. At higher temperatures the polymer was also found to undergo easily oxygenation of its backbone with atmospheric oxygen, which leads to the formation of siloxane groups.
Databáze: OpenAIRE
Externí odkaz: