Autor: Franz Dr Langhauser, Rolf Mülhaupt, David Fischer, Stephan Jüngling
Rok vydání: 1995
Předmět:
Zdroj: Angewandte Makromolekulare Chemie. 229:93-112
ISSN: 1522-9505
0003-3146
DOI: 10.1002/apmc.1995.052290106
Popis: Propene and 1-octene were copolymerized with the syndiospecific homogeneous metallocene catalyst Me2C(Cp)(Flu)ZrCl2/MAO. Large amounts of octene were incorporated randomly. While catalyst activity was not affected markedly by low octene content, molecular weight, crystallinity, Young's modulus, and glass transition temperature were reduced with increasing octene content. Blends of atactic oligopropene with syndiotactic polypropene and poly(propene-co-octene) were prepared from toluene solution and compared with a reactor blend prepared with a hybrid catalyst containing a mixture of syndiospecific Me2C(Cp)(Flu)ZrCl2/MAO and non-specific Cp2ZrCl2/MAO. Atactic oligopropene acted as plasticizer reducing Young's modulus and glass transition temperature of the blends. Propen und 1-Octen wurden mit dem syndiospezifischen Metallocen-Katalysator Me2C(Cp)(Flu)ZrCl2/MAO copolymerisiert. Es wurde ein hoher, statistischer Octeneinbau beobachtet. Niedrige Octenkonzentrationen beeinflusten die Aktivitat des Katalysators nur wenig; Molekulargewicht, Kristallinitat, E-Modul und Glastemperatur wurden dagegen mit ansteigendem Octengehalt erniedrigt. Blends aus ataktischem Oligopropen und syndiotaktischem Polypropen bzw. Poly(propen-co-octen) wurden aus einer Toluol-Losung hergestellt. Diese Losungsblends wurden mit einem Reaktorblend verglichen, der mit einem Hybrid-Katalysator bestehend aus einer Mischung von syndiospezifischem Me2C(Cp)(Flu)ZrCl2/MAO und unspezifischem Cp2ZrCl2/MAO hergestellt wurde. Das ataktische Oligopropen wirkte als Weichmacher, der E-Modul und Glastemperatur der Blends erniedrigte.
Databáze: OpenAIRE
Externí odkaz: