| Popis: |
The aim of this study was to investigate the effects of process parameters on tensile strength for PLA specimens produced by fused deposition modeling (FDM). For this purpose, two different density rates (20% and 100%), printing speeds (100 and 130 mm/s), and nozzle temperatures (180 and 220oC) with three different hatching patterns including elliptical and diagonal (Gyroid, Cross 3D ve Grid) were selected. In the study, higher tensile stress was obtained at a rate of 100%, compared to a 20% density rate. When the samples with a 20% density rate are compared among themselves, the highest tensile stress value obtained was measured as 38.76 MPa for the Grid-patterned specimen produced at a nozzle temperature of 2200C and printing speed of 100 mm/s. Statistical analysis was also done for specimens with a 20% density rate. As a result of the variance analysis (ANOVA) method, the confidence level was achieved as 96%. When comparing in terms of specific strength, it was determined that the closest pattern to the full-filled sample with a specific strength of 5,893 MPa/gr was Cross 3D-patterned sample with a value of 5.458 MPa/gr. |