| Autor: |
Jianjun Zhao, Huiqin Yun, Zhijun Hao, Xiang Jin, Huihui Li, Jinlong He, Tao Shang, Cheng Li, Xiaoxin Li |
| Rok vydání: |
2023 |
| Předmět: |
|
| Zdroj: |
Materials Express. 13:105-110 |
| ISSN: |
2158-5849 |
| DOI: |
10.1166/mex.2023.2329 |
| Popis: |
In this paper, a double perovskite oxide Gd1.8Ce0.2NiMnO6 polycrystalline sample was prepared using a conventional high temperature and solid-state reaction method. The phase formation of sample was examined using X-ray diffractometry, and the magnetic properties were measured using a PPMS. The results showed that the sample was monophase and had a space group of monoclinic P21/n. At T > TG the sample was purely paramagnetic. At TC < T < TG paramagnetic and ferromagnetic states coexisted, and Griffiths-like phase appeared in the sample. In the lower temperature region (T < TN) there was competition between ferromagnetic and antiferromagnetic states, and cluster spin-glass behavior appeared. When a magnetic field of 7 T was applied, the double perovskite oxide Gd1.8Ce0.2NiMnO6 showed a maximum −ΔSM value of 3.12296 J · kg−1 · K−1 near Curie temperature with an RCP (Refrigeration Cooling Performance) of 231.09904 J/kg. Analysis of the Arrott, recalibration and Loop curves all proved that the sample underwent a second-order phase transition. |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|