Glass-forming region and optical properties of the TeO 2 – ZnO – NiO system
| Autor: | M.F. Churbanov, J.A. Medvedeva, O.A. Zamyatin, E.V. Zamyatina, A.D. Plekhovich, S. A. Gavrin |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
010302 applied physics
Ligand field theory Materials science Non-blocking I/O Analytical chemistry chemistry.chemical_element Mineralogy 02 engineering and technology Zinc 021001 nanoscience & nanotechnology Condensed Matter Physics 01 natural sciences Electronic Optical and Magnetic Materials law.invention Nickel chemistry law 0103 physical sciences Materials Chemistry Ceramics and Composites Crystallization 0210 nano-technology Tellurium Ternary operation Glass transition |
| Zdroj: | Journal of Non-Crystalline Solids. 479:29-41 |
| ISSN: | 0022-3093 |
| Popis: | The glass-forming region of the ternary TeO2 – ZnO – NiO system has been determined using a conventional melt-quenching method under controlled condition. The stable samples containing up to 35 mol% NiO were prepared by the rapid cooling technique while a low cooling rate was allowed to obtain glasses containing 15 mol% NiO. The formation of tellurium, zinc and nickel complex oxides (e.g. NiTe2O5, Zn3Te2O8) crystalline phases in a powder batches during the glass synthesis at different temperatures were studied. Investigations of the crystallization processes in glasses showed the formation of the same complex oxides phases as in the batch. The basic thermal properties of ternary glasses were determined by DSC and an increase of glass temperature with increase in the concentration of NiO in the glass matrix was shown. The optical absorbance spectrum of the glasses exhibited three broad bands with four maxima located at about 430, 720, 810 and 1320 nm corresponding to the d-d transitions of Ni2 + ion in octahedral coordination. The ligand field, splitting and Racah parameters were calculated and its dependence on the concentration of NiO was established. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect