Effect of Water Vapor on Lifetime of 625 and 120 Foils During Oxidation Between 650 and 800 °C

Autor:	Bruce A. Pint, Marie Romedenne, Sebastien N. Dryepondt, Rishi Pillai
Rok vydání:	2021
Předmět:	Materials science Volatilisation Alloy Metals and Alloys Analytical chemistry Oxide chemistry.chemical_element Manganese engineering.material Inorganic Chemistry chemistry.chemical_compound chemistry Metallic materials Materials Chemistry engineering Water vapor FOIL method
Zdroj:	Oxidation of Metals. 96:589-612
ISSN:	1573-4889 0030-770X
DOI:	10.1007/s11085-021-10069-0
Popis:	The oxidation behavior of alloy 625 and 120 foils was studied at 650, 700 and 800 $$^\circ$$ C in dry air and flowing air + 10% H $$_2$$ O up to 10,000 h (alloy 625) or 30,000 h (alloy 120). The effect of water vapor on Cr loss was investigated. Manganese and iron in the 120 foil induced faster Cr depletion in the foil and breakdown of the Cr $$_2$$ O $$_3$$ scale into Fe and Cr-rich oxide compared to the alloy 625 foil. In the latter case, the presence of Nb led to the formation of Nb and Cr-rich oxide after breakdown of the Cr $$_2$$ O $$_3$$ scale. Simultaneous Cr loss due to oxidation and volatilization of the Cr $$_2$$ O $$_3$$ oxide scale was predicted and compared to experimental Cr loss measurements for exposures up to 30,000 h.
Databáze:	OpenAIRE
Externí odkaz:	https://explore.openaire.eu/search/publication?articleId=doi_________::4d49e5872d52f448498f6bd00e81c630 https://doi.org/10.1007/s11085-021-10069-0 Zobrazit plný text záznamu Full text from SpringerLink