A Comparison of Weldability, Structure, and Mechanical Properties of CM64 and Tribaloy T-800 Welds for Hard-Facing of Turbine Blades

Autor: Alexandre Gontcharov, Mohsen K. Keshavarz, Paul Lowden, Mathieu Brochu
Rok vydání: 2020
Předmět:
Zdroj: Journal of Manufacturing Science and Engineering. 142
ISSN: 1528-8935
1087-1357
DOI: 10.1115/1.4047142
Popis: In this study, the weldability, microstructure, and tensile properties of CM64 and Tribaloy T-800 (T800) cobalt-based hard-facing materials were studied. Successful CM64 hard-facing could be achieved at ambient temperature using manual gas tungsten arc welding (GTAW-MA). It was shown that T800 welded at ambient temperature was prone to cold cracking due to a combination of low ductility with high welding stresses that limited the accommodation of residual stresses by plastic deformation within the weld beads. Sound T800 welds of various geometries and sizes were produced on cobalt- and nickel-based X-40 and Haynes 230 superalloys, respectively, using GTAW-MA when preheating above 900 °C was used. Microstructural analyses on the sound CM64 and T800 welds were performed using optical and electron microscopy and X-ray diffraction. The distribution of elements and phases in each alloy was evaluated and revealed the epitaxial dendritic structure with the Cr–W–Si-based phase in the interdendritic region in CM64 welds compared with petal-like and equiaxed hard Mo–Co–Si-based dendrites and fine particles in T800. Tensile testing from room temperature up to 1093 °C was performed on both alloys. T800 welds possessed lower ultimate tensile strengths and elongations in this temperature range when compared with the CM64 alloy. Recommendations for hard-facing of turbine engine components were provided.
Databáze: OpenAIRE
Externí odkaz: