Effects of strain rate on mechanical properties and deformation behavior of an austenitic Fe-25Mn-3Al-3Si TWIP-TRIP steel
Autor: | Jake T. Benzing, James Bentley, Dierk Raabe, Kip O. Findley, D.T. Pierce, Whitney A. Poling, James E. Wittig |
---|---|
Rok vydání: | 2018 |
Předmět: |
010302 applied physics
Materials science Mechanical Engineering Twip Metallurgy TRIP steel 02 engineering and technology Strain rate 021001 nanoscience & nanotechnology Condensed Matter Physics 01 natural sciences Deformation mechanism Mechanics of Materials 0103 physical sciences Ultimate tensile strength General Materials Science Slow strain rate testing Dislocation Composite material Deformation (engineering) 0210 nano-technology |
Zdroj: | Materials Science and Engineering: A. 711:78-92 |
ISSN: | 0921-5093 |
DOI: | 10.1016/j.msea.2017.11.017 |
Popis: | The effects of quasi-static and low-dynamic strain rate ( e = 10−4 /s to e = 102 /s) on tensile properties and deformation mechanisms were studied in a Fe-25Mn-3Al-3Si (wt%) twinning and transformation-induced plasticity [TWIP-TRIP] steel. The fully austenitic microstructure deforms primarily by dislocation glide but due to the room temperature stacking fault energy [SFE] of 21 ± 3 mJ/m2 for this alloy, secondary deformation mechanisms such as mechanical twinning (TWIP) and epsilon martensite formation (TRIP) also play an important role in the deformation behavior. The mechanical twins and epsilon-martensite platelets act as planar obstacles to subsequent dislocation motion on non-coplanar glide planes and reduce the dislocation mean free path. A high-speed thermal camera was used to measure the increase in specimen temperature as a function of strain, which enabled the use of a thermodynamic model to predict the increase in SFE. The influence of strain rate and strain on microstructural parameters such as the thickness and spacing of mechanical twins and epsilon-martensite laths was quantified using dark field transmission electron microscopy, electron channeling contrast imaging, and electron backscattered diffraction. The effect of sheet thickness on mechanical properties was also investigated. Increasing the tensile specimen thickness increased the product of ultimate tensile strength and total elongation, but had no significant effect on uniform elongation or yield strength. The yield strength exhibited a significant increase with increasing strain rate, indicating that dislocation glide becomes more difficult with increasing strain rate due to thermally-activated short-range barriers. A modest increase in ultimate tensile strength and minimal decrease in uniform elongation were noted at higher strain rates, suggesting adiabatic heating, slight changes in strain-hardening rate and observed strain localizations as root causes, rather than a significant change in the underlying TWIP-TRIP mechanisms at low values of strain. |